Wet Process PU Resin for Microfiber
Wet Process PU Resin for Microfiber
Wet-process PU Resin for NaOH Reduction Microfiber
| Name | Viscosity (Pa·s/25℃) | Solid (%) | Solvents | 100% Modulus (MPa) | Tensile Strength (MPa) | Elongation (%) | Characteristics | Applications |
| WR-1 | 40~60 | 29.0~31.0 | DMF | 3.0 | 60.0 | 600 | soft grade, hydrolysis resistance, acid resistant, alkali resistant, good dyeing property | NaOH reduction |
| WR-2 | 50~80 | 29.0~31.0 | DMF | 6.0 | 60.0 | 600 | mid-soft grade, hydrolysis resistance, acid resistant, alkali resistant, good dyeing property, good resilience | NaOH reduction |
| WR-3 | 40~60 | 29.0~31.0 | DMF | 9.0 | 70.0 | 470 | mid-hard grade, hydrolysis resistance, acid resistant, alkali resistant, good dyeing property | NaOH reduction |
Wet-process PU Resin for TOL Reduction Microfiber
| Name | Viscosity (Pa·s/25℃) | Solid (%) | Solvents | 100% Modulus (MPa) | Tensile Strength (MPa) | Elongation (%) | Characteristics | Applications |
| WR-4 | 80~120 | 29.0~31.0 | DMF | 2.0 | 55.0 | 740 | soft grade, anti-TOL extracting, hydrolysis resistant, acid resistant, alkali resistant | TOL reduction |
| WR-5 | 80~120 | 29.0~31.0 | DMF | 6.0 | 60.0 | 600 | mid-soft grade, anti-TOL extracting, hydrolysis resistant, acid resistant, alkali resistant | TOL reduction |
| WR-6 | 80~120 | 29.0~31.0 | DMF | 9.0 | 65.0 | 650 | mid-hard grade, anti-TOL extracting, hydrolysis resistant, acid resistant, alkali resistant | TOL reduction |
| WR-7 | 80~120 | 29.0~31.0 | DMF | 15.0 | 60.0 | 500 | hard grade, anti-TOL extracting, hydrolysis resistant, acid resistant, alkali resistant | TOL reduction |
Wet-process PU Resin for TOL Reduction and Low-cost Microfiber
| Name | Viscosity (Pa·s/25℃) | Solid (%) | Solvents | 100% Modulus (MPa) | Tensile Strength (MPa) | Elongation (%) | Characteristics | Applications |
| WR-8 | 160~220 | 29.0~31.0 | DMF | 5.0 | 55.0 | 700 | mid-soft grade, anti-TOL extracting, low-cost type | TOL reduction |
| WR-9 | 80~120 | 29.0~31.0 | DMF | 15.0 | 52.0 | 500 | hard grade, anti-TOL extracting, low-cost type | TOL reduction |
Wet-process PU Resin for TOL Reduction and Good Resilience Microfiber
| Name | Viscosity (Pa·s/25℃) | Solid (%) | Solvents | 100% Modulus (MPa) | Tensile Strength (MPa) | Elongation (%) | Characteristics | Applications |
| WR-10 | 80~120 | 29.0~31.0 | DMF | 6.0 | 60.0 | 600 | mid-soft grade, anti-TOL extracting, hydrolysis resistance, acid resistant, alkali resistant, good resilience | TOL reduction |
Wet-process PU Resin for TOL Reduction and Thin Shirring Microfiber
| Name | Viscosity (Pa·s/25℃) | Solid (%) | Solvents | 100% Modulus (MPa) | Tensile Strength (MPa) | Elongation (%) | Characteristics | Applications |
| WR-11 | 80~120 | 29.0~31.0 | DMF | 6.0 | 60.0 | 600 | mid-soft grade, anti-TOL extracting, hydrolysis resistance, acid resistant, alkali resistant, thin shirring | TOL reduction |
| WR-12 | 120~150 | 29.0~31.0 | DMF | 10.0 | 75.0 | 750 | mid-hard grade, anti-TOL extracting, hydrolysis resistance, acid resistant, alkali resistant, thin shirring | TOL reduction |
We are a China-based wet process PU resin for microfiber manufacturer. Our company has built up a complete research, manufacture and sales system. We are involved in the production of PU resins including dry process PU resin, wet process PU resin, wet process PU resin for microfiber, water based polyurethane resign for surface layer, etc. Our products are ISO9001 certified. Contact us for the PU resin for microfiber you are looking for. Thank you!